WELDING ELECTRODES

LASER B 55-S
( E7018-1H4 )

Suitability for use in welding of high-strength, fine-grained steels, CTOD tested., High ductility at low temperatures down to -60°C, It is used for joining thick materials safely, Weld metal recovery of approx. 120%, Requirement of re-drying for minimum 2 hours at the temperatur...

LASER B 60
( E7018H4 )

Suitability for use in out-of-position welding except for welding at vertical down position, Excellent strength and toughness, Suitability for use in the fields of steel constructions, boiler, container, machine manufacturing and shipbuilding as well as for use in welding low pur...

TEMPO B 48
( E7018-GH4 )

This is AC/DC basic-coated electrode that has a weld metal recovery of 120% which can be used at all welding positions except for the vertical down position, Usable with short arc in (-) pole for root pass welding with excellent penetration, especially at vertical-up position, We...

TEMPO B 60
( E8018-GH4 )

Content with Mn-Ni alloy, High toughness and high resistance to cracking, Suitability for use in welding high strength, fine-grained structural steels, Suitability for use in welding of materials with service temperatures between -60°C and +350°C, Very high values of impact resis...

TEMPO B 63
( E8018-GH4 )

Suitability for use in welding carbon and low-alloyed high-strength steels with carbon contents up to 0.6%, Suitability for use in rail-joint welding, Ductile and crack-resistant weld metals, Recovery of weld metals about 115%, Weldability at all positions except for vertical dow...

TEMPO B 65
( E8018-GH4 )

Basic type Ni-Mo alloy thick coated electrode. Suitability for use in welding high-strength, fine-grained steels, Consistent high ductility and crack-resistance at low working temperatures down to -60°C, Resistance to aging, CTOD tested., Convenience of welding at all positions e...

TEMPO B 70 M
( E9018MH4 )

High-strength fine-grained structural steels and cast steel welding., Low amounts of Hydrogen (4ml / 100g), Operability at temperatures between - 60°C and + 350°C, Low content of moisture absorbed during long-term storage, Re-drying: 300-350°C / min. 2h

TEMPO B 70 S
( E9018-GH4 )

Suitability for use in welding of high-strength , fine-grained steels, High ductility and high resistance to cracking obtained in welding fine-grained steels, Suitability for use in welding of materials with service temperatures between -60°C and +350°C, Welding of the all-weld m...

TEMPO B 70 Mo
( ~E9018-D1H4 )

Suitability for use in welding high-strength, fine-grained constructional steels and high-temperature steels, Use in welding rail steels with strength values up to 785 N/mm2, Content including Mn-Mo alloy, Resistance to cracking as well as to aging, high toughness, Welding of the...

TEMPO B 75
( E10018-GH4 )

Basic type Mn-Mo-Ni alloyed, thick coated electrode., High ductility and high resistance to cracking obtained in welding high-strength, quenched and tempered, fine-grained structural steels, Suitability for use in welding of materials with service temperatures between -60°C and +...

TEMPO B 85 M
( E11018-MH4 )

Basic-type coated and Ni-Cr-Mo -alloyed electrode character, Applicability in welding of casting steels and high-strength fine-grained steels, Weld metals with high resistance to cracking., Low amounts of hydrogen (4 ml per 100 g of weld metal), Low amounts of moisture absorbed d...

TEMPO B 90
( E12018-GH4 )

Suitability for use in welding of Ni-Cr-Mo alloyed steels, fine-grained steels, cementation steels, tempered steels, cast steels etc., Suitability for use of applications requiring a minimum tensile strength value of 830 N/mm2, Welding of the all-weld metal test assembly shall be...

TEMPO Ni Cu
( E7018-G/7018-W1 (mod.)H4 )

Content of Ni-Cu-Cr alloy, Suitability for use in welding structural steels exposed to weathering, such as COR-TEN., High mechanical properties with excellent crack resistance, Convenience of welding at all positions except for vertical down position, Weld deposits with very low...

TEMPO B W2
( E8018-W2H4 )

Content of Ni-Cu-Cr alloy, Suitability for use in welding structural steels exposed to weathering, especially for COR-TEN B type steels., High mechanical properties with excellent crack resistance, Convenience of welding at all positions except for vertical down position, Weld de...

TEMPO B 1
( E8018-C3H4 )

Suitability for use in welding low-alloyed steels resistant to lower service temperatures, Serviceability of weld metals at temperatures down to -60°C, Weld metal recovery of approx. 120%, Re-drying: 300-350°C / min. 2h

TEMPO B 2
( E8018-C1H4 )

Suitability for use in welding fine-grained, Ni-alloyed and carbon steels as well as cryogenic steels, High ductility and crack resistance in weld deposits, Serviceability of weld metals at temperatures down to -80°C, Weld metal recovery of approx. 120%, Convenience of welding at...

TEMPO B 3
( E8018-C2H4 )

Suitability for use in welding Ni-alloyed construction steels for cryogenic applications, High ductility and crack resistance in weld deposits, Serviceability of weld metals at temperatures down to -110°C

OPUS MOR

Welding of heat-resistant Mo-alloyed, fine-grained or unalloyed steels used for construction of boilers and pipes, Weld metal is resistant to working temperatures up to +550°C, Preheat and interpass temperature should be used below 200 °C, Electrodes of this type give a smooth dr...

OPUS MOB
( E7018-A1H4 )

Electrodes with basic covering are usually suitable only for direct current, electrode positive., Welding of heat-resisting, Mo-alloyed, fine grained and unalloyed steels used for construction of boilers and pipes, Weld metal is resistant to working temperatures from -50°C to +55...

OPUS C
( E8013-G )

Welding of steam production plant equipments, steam pipes and similar kinds of heat-resistant joints, all of which are made of Cr-Mo alloy steels, Electrode coating of rutile character, Resistance of weld metal to operating temperatures of values up to 570°C, Preheat and interpas...