WELDING ELECTRODES

OPUS CM
( E8018-B2H4 )

Used in welding of heat and pressure resistant steam boilers and pipes made of Cr-Mo alloy steels, refinement steels, cementation steels and nitride steels., Weld metal withstands operating temperatures up to + 570 °C., Electrode coating of basic character, Preheat and interpass...

OPUS CM-15
( E8015-B2H4 )

Welding of steam boilers and steam pipes made of Cr-Mo alloyed heat resistant steels, cementation steels, nitrided steels, Resistance of weld metal to operating temperatures of values up to 570°C., Weld metal recovery of approx. 125%, It can be used in position welding with lower...

OPUS CML
( E7018-B2LH4 )

Applicability in welding heat-resisting , low-alloyed steels, Suitability to use against corrosion in sour crude, and against stress corrosion in petrochemical industry, Preheat and interpass temperature should be used at 150-250 °C., The test assembly shall be cooled in the furn...

OPUS CMV
( E9018-GH4 )

V-alloyed steels such as 14MoV6-3, Electrode coating of basic character, Serviceability at temperatures up to 580°C, Pre-heating and interpass temperatures : 200°C-300°C, The test assembly shall be cooled in the furnace to 300 °C at a rate not exceeding 200 °C/h, Re-drying: 300-3...

OPUS 2 CM
( E9018-B3H4 )

Welding of steam boilers, steam pipes made of Cr-Mo-alloyed steels, nitrided steels, not-heat treated cementation steels, Resistance of weld metal to working temperatures up to 600°C, Preheat and interpass temperature should be used at 200-300 °C, The test assembly shall be coole...

OPUS 2 CM-15
( E9015-B3H4 )

Welding of steam boilers, steam pipes made of Cr-Mo-alloyed steels, nitrided steels, not-heat treated cementation steels, Resistance of weld metal to working temperatures up to 600°C, Preheat and interpass temperature should be used at 200-300 °C, The test assembly shall be coole...

OPUS 2 CML
( E8018-B3LH4 )

Applicability in welding of heat-resisting steels containing 2% Cr - 1% Mn and similar alloys, Electrode with basic-type coating, Formation of more ductile and less hard weld metal due to low carbon content, Serviceability at temperatures of values up to 600 °C, Preheat and inter...

OPUS 5 CM
( E8018-B6(E 502-15)H4 )

Used in high-heat-resistant steels, high strenth cementation steels, petro chemical industry and on pressured hydrogen tanks., Serviceability of weld metal at working temperature up to 650°C, Preheat and interpass temperature should be used at 200-230 °C, The test assembly shall...

OPUS 9 CM
( E8018-B8(E505-15)H4 )

Welding of boilers, pressure vessel steels, pipe steels and cast steels, Electrode coating of basic character, Electrode content of % 9 Chromium, % 1 Molybdenum, Resistance of weld metal to working temperatures up to 650°C, Preheat and interpass temperature should be used at 20...

OPUS 9 CM-15
( E8015B8H4 )

Heat resistance and low hydrogen electrode with basic-type coating, Resistance of weld metal to working temperatures up to 650°C. Suitable for 9 Cr% and 1 Mo% steels., Welding of pressurized boiler steels, pipe steel and steel castings., Preheat and interpass temperature should b...

OPUS 9 CMV
( E9018-B9H4 )

Recomended holding time 4h for heat treatment., It is a high alloyed, basic coated electrode with low hydrogen content. It shows high creep strength and toughness even when exposed to stress for a long time., Recommended for use in steam producing plants, steam pipes and welding...

OPUS 9 CMV-15
( E9015-B9H4 )

It is a high alloyed, basic coated electrode with low hydrogen content. It shows high creep strength and toughness even when exposed to stress for a long time., Recommended for use in steam producing plants, steam pipes and welding of similar Cr-Mo alloyed steels., Weld metal’s r...

OPUS P92
( E9018-B9(mod.) )

Used in welding of heat resistant T/P92 and Cr-Mo alloyed similar steels used in power generation plants and steam pipes., Provides creep strength and toughness at elevated temperatures with additional alloying elements, Weld metal is resistant to temperatures up to +650°C, Brusc...

ELOX B 307
( ~E307-15 )

Dissimilar joints, tough buffer and intermediate layers prior to hardfacing, 14Mn-steels, 13 – 17% Cr and heat resistant Cr and austenitic steels up to 850ºC, armor plates, high carbon and quenched and tempered steels, surfacing of gears, valves, turbine blades, etc. For joint we...

ELOX R 307
( ~E307-16 )

Dissimilar joints, tough buffer and intermediate layers prior to hardfacing, 14Mn-steels, 13 – 17% Cr and heat resistant Cr and austenitic steels up to 850ºC, armor plates, high carbon and quenched and tempered steels, surfacing of gears, valves, turbine blades, etc. For joint we...

ELOX B 307L
( E307-15 )

Especially developed for the welding of armor steel. Therefore this product using for hot work tool steels. It is suitable for welding steels that are difficult to use., Weld metal is resistant to crack, impact, rust and abrasion., Stainless - Chromium, Chromium - Nickel steels a...

ELOX RS 307
( ~E307-26 )

Welding of high resistant alloyed / unalloyed steels, heat resistant steels / stainless steels, steels wit 14%Mn, for problematic steels., Joint and filler welding of different metals., Rutile coated electrode, weld metal is austenitic, resistant to thermal shocks, keeps its thou...

ELOX R 308 L
( E308L-16 )

Rutile coated low carbon electrode Used for the welding of food tanks, acid, gas, steam and water fittings, stainless Cr steels and corrosion resistant materials in the chemical industry, Resistant to corrosion and cracks., Working temperature is up to +350 °C, Re-drying: 120-200...

ELOX R 308 L-17
( E308L-17 )

Rutile coated low carbon electrode Used for the welding of food tanks, acid, gas, steam and water fittings, stainless Cr steels and corrosion resistant materials in the chemical industry, Resistant to corrosion and cracks., Working temperature is up to +350 °C, Re-drying: 120-200...

ELOX R 308 H
( E308H-16 )

Electrode with rutile coating on alloyed core-wire, Applicability in welding Cr-Ni alloyed austenitic high temperatures steels, Usability in welding at all positions except for vertical downward position, Applicability in joint welding and surfacing of heat resisting similar type...